Abstract

The stress corrosion cracking (SCC) tendencies of several engineering alloys were studied in an acidified seawater environment as a function of applied strain rate and electrolyte temperature. The selected alloys included austenitic stainless steels 304L, 316L, 904L and A-286 (an iron-based superalloy at two heat treatments yielding ultimate tensile strengths of 130 and 200 ksi), Inconel 718 (220 ksi ultimate tensile strength) and Hastelloys C-22 and C-276. The slow strain rate test technique was used to evaluate the SCC strain rate dependency of each alloy at extension rates of 4.7 x 10^-6, 4.7 x 10^-4 and 4.7 x 10^-3 mm/sec. The effect of electrolyte temperature was evaluated at 38C and 60C at a single extension rate of 4.7 x 10^-5 mm/sec. Control specimens were tested in a laboratory air environment at an extension rate of 4.7 x 10^-5 mm/sec. Various mechanical parameters of the specimens tested in the corrosive medium were compared with those of control specimens to quantify the degree of cracking. Fractographic evidence of SCC was obtained using scanning electron microscopy (SEM). An attempt was made to correlate SCC tendency with the alloy's passivation kinetics and microstructure. Atmospheric exposure testing was performed in a simulated space shuttle launch pad environment for selected alloys.

Extent

191 p.

Comments

College of Engineering and Computer Science|FAU Electronic Theses and Dissertations Collection|Thesis (M.S.)--Florida Atlantic University, 1992.|College of Engineering and Computer Science

Identifier

FADT14853

Format

pdf

Download

Share

COinS